This product is a uniform, transparent, colorless, non-toxic and environmentally friendly particle. It is a polymer alloy material modified by blending ABS and PVC, which improves the impact strength and flame retardant performance of a single component ABS and reduces the cost of ABS; Simultaneously improving the heat resistance, density, and processing performance of PVC. Mainly used in industries such as electronics, light industrial appliances, automobiles, and construction.
| ITEMS | STANDARD | UNIT | CONDITION | RESULTS |
| MFI | ISO 1133 | g/10min | 260℃ 5kg | 27 |
| Density | ISO 1183 | g/cm3 | 23℃ | 1.105 |
| Tensile Strength | ISO 527 | MPa | 50mm/min 23℃ | 54 |
| Elongation at Breaking | ISO 527 | % | 50mm/min 23℃ | 32 |
| Bending Strength | ISO 178 | MPa | 2mm/min 23℃ | 81 |
| Bending modulus | ISO 178 | MPa | 2mm/min 23℃ | 2294 |
| Simply Supported Beam Notch Impact Strength | ISO 179 | kJ/m2 | 23℃ 4J | 51 |
| ISO 179 | kJ/m2 | -30℃ 4J | 48 | |
| Cantilever Beam Notch Impact Strength | ISO 180 | kJ/m2 | 23℃ 5.5J | – |
| ISO 180 | kJ/m2 | -30℃ 5.5J | – | |
| Hot Deformation Temperature | ISO D648 | ℃ | 1.8MPa | 95 |
| ℃ | 0.45MPa | 108 | ||
| Burning Level | UL-94 | – | – | 1.5mm HB |
| Forming Shrinkage Rate | 294-4 | % | – | 0.4-0.6 |
Huahui Plastics is mainly committed to exploring, developing, and manufacturing new products, technologies, and materials in the plastic industry: